Preparation of NASICON Silico Phosphates of Composition Na1 + xZr2SixP3 – xO12 by Pyrolysis of Solution in Melt

Capa

Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

A new method for preparing Na1 + xZr2SixP3 – xO12 (0 < x < 3) based on pyrolysis of solution containing a mixture of organic components in rosin melt has been proposed. Effect of superstoichiometric amounts of sodium and phosphorus on the phase composition of synthesis products has been proved. It has been found that precursor for the sample of maximal purity of phase composition is prepared at molar ratio Na : Zr : Si : P = (1.15 + x) : 2 : x : (y – x), where y = 3 (1.20 + x)/(1 + x). Precursor calcination temperature is 1000°C. Different NASICON compositions without crystalline admixtures have been obtained in the range 1.5 ≤ x ≤ 2.12. The prepared samples have been studied by X-ray powder diffraction and scanning electron microscopy. The disclosed method of synthesis is promising for the preparation of NASICON as both bulk materials and thin layer coatings.

Sobre autores

D. Grishchenko

Institute of Chemistry, Far Eastern Branch, Russian Academy of Sciences

Email: grishchenko@ich.dvo.ru
690022, Vladivostok, Russia

M. Medkov

Institute of Chemistry, Far Eastern Branch, Russian Academy of Sciences

Autor responsável pela correspondência
Email: grishchenko@ich.dvo.ru
690022, Vladivostok, Russia

Bibliografia

  1. Hong H.Y.-P. // Mater. Res. Bull. 1976. V. 11. № 2. P. 173. https://doi.org/10.1016/0025-5408(76)90073-8
  2. Goodenough J.B., Hong H.Y.-P., Kafalas J.A. // Mater. Res. Bull. 1976. V. 11. № 2. P. 203. https://doi.org/10.1016/0025-5408(76)90077-5
  3. Miyachi Y., Sakai G., Shimanoe K., Yamazoe N. // Sens. Actuators, B. 2003. V. 93. № 1–3. P. 250. https://doi.org/10.1016/S0925-4005(03)00174-6
  4. Paściak G., Mielcarek W., Prociów K., Warycha J. // Ceram. Int. 2014. V. 40. № 8. P. 12783. https://doi.org/10.1016/j.ceramint.2014.04.132
  5. Meunier M., Izquierdo R., Hasnaoui L. et al. // Appl. Surf. Sci. 1998. V. 127–129. P. 466. https://doi.org/10.1016/S0169-4332(97)00674-0
  6. Tetsuya K., Miyachi Y., Shimanoe K., Yamazoe N. // Sens. Actuators, B. 2001. V. 80. № 1. P. 28. https://doi.org/10.1016/S0925-4005(01)00878-4
  7. Kim H.J., Choi J.W., Kim S.D., Yoo K.S. // Mater. Sci. Forum. 2007. V. 544–545. P. 925. https://doi.org/10.4028/www.scientific.net/MSF.544-545.925
  8. Jalalian-Khakshour A., Phillips Ch., Jackson L. et al. // J. Mater. Sci. 2020. V. 55. P. 2291. https://doi.org/10.1007/s10853-019-04162-8
  9. Naqash S., Sebold D., Tietz F., Guillon O. // J. Am. Ceram. Soc. 2019. V. 102. № 3. P. 1057. https://doi.org/10.1111/jace.15988
  10. Yang G., Zhai Y., Yao J. et al. // Chem. Commun. 2021. V. 57. P. 4023. https://doi.org/10.1039/d0cc07261c
  11. Noguchi Y., Kobayashi E., Plashnitsa L.-S. et al. // Electrochim. Acta. 2013. V.101. P. 59. https://doi.org/10.1016/j.electacta.2012.11.038
  12. Fuentes R.O., Marques F.M.B., Franco J.I. // Bol. Soc. Esp. Ceram. Vidrio. 1999. V. 38. № 6. P. 631.
  13. Fuentes R.O., Figueiredo F., Marques F.-M.B., Franco J.I. // Solid State Ionics. 2001. V. 139. № 3–4. P. 309. https://doi.org/10.1016/S0167-2738(01)00683-X
  14. Fuentes R.O., Figueiredo F.M., Marques F.M.B., Franco J.I. // Solid State Ionics. 2001. V. 140. № 1–2. P. 173. https://doi.org/10.1016/S0167-2738(01)00701-9
  15. Shimizu Y., Azuma Y., Michishita S. // J. Mater. Chem. 1997. V. 7. P. 1487.
  16. Naqash S., Tietz F., Yazhenskikh E. et al. // Solid State Ionics. 2019. V. 336. P. 57. https://doi.org/10.1016/j.ssi.2019.03.017
  17. Грищенко Д.Н., Курявый В.Г., Подгорбунский А.Б., Медков М.А. // Журн. неорган. химии. 2023. № 1. С. 17. https://doi.org/10.31857/S0044457X22601043
  18. Грищенко Д.Н., Дмитриева Е.Э., Медков М.А. // Хим. технология. 2022. Т. 23. № 10. С. 418. https://doi.org/10.31044/1684-5811-2022-23-10-418-423
  19. Narayanan S., Reid S., Butler S., Thangadurai V. // Solid State Ionics. 2019. V. 331. P. 22. https://doi.org/10.1016/j.ssi.2018.12.003
  20. Rao Y.B., Bharathi K.K., Patro L.N. // Solid State Ionics. 2021. V. 366–377. P. 115671. https://doi.org/10.1016/j.ssi.2021.115671
  21. Wang H., Zhao G., Wang S. et al. // Nanoscale. 2022. V. 14. № 3. P. 823. https://doi.org/10.1039/d1nr06959d

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML
Baixar
2.

Baixar (254KB)
Metadados
3.

Baixar (83KB)
Metadados
4.

Baixar (170KB)
Metadados
5.

Baixar (324KB)
Metadados
6.

Baixar (1MB)
Metadados

Declaração de direitos autorais © Д.Н. Грищенко, М.А. Медков, 2023